脉冲电沉积镍-铜合金

采用脉冲电沉积技术在304不锈钢表面制备Ni-Cu合金镀层,镀液组成和工艺条件为:NiSO4ꞏ6H2O 200g/L,CuSO4ꞏ5H2O 10 g/L,十二烷基硫酸钠0.2 g/L,柠檬酸钠80 g/L,糖精0.2 g/L,pH 4.0,温度25°C,搅拌速率30 r/min,平均电流密度40~120 mA/cm2,脉冲频率0~100 Hz,占空比20%~90%,时间30 min。研究了平均电流密度、脉冲频率和占空比对Ni-Cu合金镀层的元素组成、表面形貌和显微硬度的影响,得到较优的工艺参数为:平均电流密度40 mA/cm2,脉冲频率50 Hz,占空比60%。该条件下所得Ni-Cu合金镀层由质量分数分别为56.53%和43.47%的Ni和Cu组成,呈“菜花”状形貌,结晶细致、均匀,显微硬度为614.4 HV。     

Investigation on phase shifting for a 4 K Stirling pulse tube cryocooler with He-3 as working fluid

He-3 is generally recognized for its ability to provide more excellent thermophysical performance than He-4, especially in the 4 K temperature range. However, this was not always the case in our preliminary experiments on a three-stage Stirling-type pulse tube cryocooler (SPTC). Our ongoing studies, as reported in this paper, demonstrate that the different working fluids also affect the performance through their phase shifting capability. This feature has been passed over in large part by researchers considering refrigerant substitution. Unlike previous theoretical analyses that focus primarily on regenerator losses, this report investigates the effects of the working fluid on the phase angle at the cold end in order to quantitatively reveal the relationship between the lowest attainable temperature and the cooling capacity. The analysis agrees well with our experimental results on a three-stage SPTC. While running with the operating parameters optimized for He-3, the lowest temperature of the SPTC decreased from 5.4 K down to 4.03 K. This is the lowest refrigeration temperature ever achieved with a three-stage SPTC.     

Microstructure,tribological behavior and magnetic properties of Fe−Ni−TiO2 composite coatings synthesized via pulse frequency variation

The Fe−Ni−TiO₂ nanocomposite coatings were electrodeposited by pulse frequency variation. The results showed that the nanocomposite with a very dense coating surface and a nanocrystalline structure was produced at higher frequencies. By increasing the pulse frequency from 10 to 500 Hz, the iron and TiO₂ nanoparticles contentswere increased in expense of nickel content. XRD patterns showed that by increasing the frequency to 500 Hz, an enhancement ofBCC phase was observed and the grain size of deposits was reduced to 35 nm. The microhardness and the surface roughness were increased to 647 HV and 125 nm at 500 Hz due to the grain size reduction and higher incorporation of TiO₂ nanoparticles into the Fe−Ni matrix (5.13 wt.%). Moreover, the friction coefficient and wear rate values were decreased by increasing the pulse frequency;while the saturation magnetization and coercivity values of the composite deposits were increased.     

Application of differential evolution for cascaded multilevel VSI with harmonics elimination PWM switching

Harmonic elimination pulse width modulation (HEPWM) method has been widely applied to multilevel voltage source inverter (MVSI) to remove low frequency harmonics from its output voltage. However, the computation of the HEPWM switching angles for MVSI is very challenging due to several constraints, namely angle sequencing, very tight angular spacing and the numerous possibilities of angles distribution ratio. Realizing the potential of Differential Evolution (DE) to handle complex problems, this work proposes its application to solve the HEPWM problem for cascaded MVSI. Its emphasis is on improving the availability of HEPWM for higher output voltage by extending the maximum range of modulation index (M). It also removes the discontinuities in the switching angles and reduces the number of distribution ratio required to obtain the required solution. Compared to the most advanced (similar) work, i.e., 7-level MVSI with seventeen switching angles, DE covers a wider range of M; the maximum achievable M is 2.80. Furthermore, it exhibits very low second order distortion factor (DF₂): for the worst case, the value of DF₂ is 0.0014%. To verify the viability of the proposed algorithm, simulation is carried out and hardware prototype is constructed. Both results show very good agreement with the theoretical prediction.     

工艺参数对超声辅助脉冲电沉积镍-氮化钛复合镀层的影响

在45钢表面以超声波辅助脉冲电沉积制备Ni-TiN复合镀层。研究了平均阴极电流密度、脉冲占空比、超声功率和TiN粒子(平均直径20~30 nm)添加量对复合镀层的TiN粒子含量和显微硬度的影响。得到较优的工艺参数为:NiSO4ꞏ6H2O 300 g/L,NiCl2ꞏ6H2O 30 g/L,H3BO330 g/L,十二烷基硫酸钠0.3 g/L,TiN 25 g/L,pH 4.1~4.3,温度40°C,平均阴极电流密度4 A/dm2,脉冲占空比40%,脉冲频率1000 Hz,超声功率300 W,机械搅拌速率200 r/min,时间60 min。该条件下所得Ni-TiN复合镀层的TiN质量分数为8.35%,显微硬度为819 HV,表面平整、致密,晶粒尺寸均匀。     

极薄、超宽规格装甲板压力淬火工艺数值模拟优化

利用数值模拟的方法对极薄、超宽规格装甲板淬火过程的畸变进行了模拟研究,并对脉冲式压力淬火的控制参数进行了优化。通过对比不同冷却条件装甲板的变形量,确定了脉冲式压力淬火的脉冲压力和周期。结果表明,脉冲约束的模拟条件下,装甲板在厚度Z方向上的最终变形量为1.7 mm,不仅小于2 mm的标准要求,而且可以实现装甲板的小淬火畸变前提下满足其表面无压痕、划痕等其他损伤的实际生产需求。     

基于一种改进逐点比较插补法的激光打标机控制加工算法

在激光打标系统中,逐点比较插补法是一种普遍使用的算法。这种算法在控制激光运动轨迹和对图像轨迹的拟合过程中,起到极其重要的作用。由于逐点比较插补法具有运算直观,脉冲输出均匀,调节方便等特点,所以是一种较为适合打标机系统应用的插补算法。但是传统的逐点比较插补算法存在精度低和速度慢等问题。为了改善该算法的性能,对传统逐点比较插补算法进行了改进,并进行了计算和模拟仿真。结果表明改进比较插补算法在精度和速度上都有明显提高。     

掺铒单模光纤飞秒脉冲激光器和放大器

为了获得一种被动锁模掺铒光纤振荡器及功率放大器，数值模拟出超短脉冲在光纤中的传输和演化过程，并基于此搭建了一种被动锁模掺铒光纤飞秒振荡器及功率放大器。实验获得了中心波长1560 nm、重复频率100 MHz、输出功率30 mW、脉冲宽度85 fs超短脉冲。通过采用PPLN晶体进行倍频，进一步获得了输出功率5 mW，中心波长780 nm的飞秒脉冲。该光纤激光器为全保偏光纤结构，具有体积小巧、可靠性高、稳定性好的特点。     

高强铝合金双脉冲VPPA焊缝成形机理

建立双脉冲VPPA(variable polarity plasma arc)焊接系统，进行7A52高强铝合金双脉冲VPPA焊接工艺试验，研究低频脉冲调制叠加高频脉冲对VPPA焊接过程中焊缝成形和焊缝力学性能的影响. 结果表明，低频脉冲周期性振荡液态熔池，可获得表面饱满的鱼鳞纹焊缝；高频脉冲使电弧更为集中，有效地提高了电弧能量密度，穿透力加强；双脉冲耦合振荡加强了对熔池的搅动作用细化了铝合金焊缝晶粒. 焊接接头抗拉强度达到384.13 MPa，相比VPPA焊接接头强度提高了10.21%左右；焊接接头断面收缩率和断后伸长率均有一定程度的提高. 铝合金双脉冲VPPA焊接工艺提高了焊接接头力学性能.     

激光脉冲编码抗有源干扰效果研究

激光脉冲编码是激光制导武器的抗干扰措施之一。角度欺骗式干扰和高重频干扰是目前半主动激光制导武器的主要有源干扰来源。为研究不同激光脉冲编码方式对激光半主动制导武器抗这两种干扰性能的影响,本文针对敌方激光告警机的识别算法与我方导引头的解码过程,提出自相关函数与归一化互相关函数评价方法,并对目前主要编码方式进行仿真,仿真结果表明:激光脉冲编码的抗角度欺骗式干扰能力受编码序列周期性与脉冲间隔随机性的影响；抗高重频激光干扰能力受编码序列脉冲间隔随机性的影响；LFSR状态码的抗角度欺骗式干扰与抗高重频干扰效果均优于其他编码方式。